MADE OF WOVEN HIGH DENSITY BLACK POLYETHYLENE FIBRES,
WARP X WEFT:12/14 X 12/14 PER SQUARE INCH, LAMINATED ON BOTH SIDES WITH LOW DENSITY POLYETHYLENE;
STABILIZED AGAINST ULTRAVIOLET RAYS AND EXCESS HEAT FOR LONG OUTDOOR EXPOSURE.
MAX. 5% LOSS ON ORIGINAL TENSILE STRENGTH UNDER ISO 1421 AFTER 1500 HOURS UV UNDER ASTM 653/94 (UVB 313 MPEAK)
MATERIAL WEIGHT: MINIMUM 200 GR/M2 +/- 5% TENSILE STRENGTH: MINIMUM 600 N BOTH DIRECTIONS OF WARP AND WEFT (BS 2576, 50 MM GRAB TEST, OR EQUIVALENT);
TEAR RESISTANCE: MINIMUM 100 N BOTH DIRECTIONS (BS 4303 WING TEAR OR EQUIVALENT); FLAMMABILITY (CPAI 84-1995, SECTION 6): ABOVE 200 DEGREES C;